Polyester PE PP Acrylic PPS P84 Nomex Aramid PTFE Dust Collector Filter Cloth Bag
| Construction |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
| Fibre Composition |
polyester |
polypropylene |
PPS |
polyimide |
Acrylic |
Aramid/Nomex |
FMS |
PTFE Fiber |
| Scrim Composition |
polyester |
polypropylene |
PPS |
polyimide |
Acrylic |
Aramid/Nomex |
fiberglass |
pffe |
| Felt Area Weight |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
850g/m2(±5%) |
750g/m2(±5%) |
| Thickness |
1.8-2.0mm |
2-2.1mm |
1.7-1.9mm |
1.9-2.1mm |
1.7-2.1mm |
1.9-2.1mm |
2.8mm |
1.3-1.7mm |
| Mean Air Permeability |
10-15 m3/m2/min at 12.7mmH2O |
10-12 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
8-12 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
8-15 m3/m2/min at 12.7mmH2O |
2-5 m3/m2/min at 12.7mmH2O |
| Breaking Strength-MD(warp) |
900 N / 5cm |
1000 N / 5cm |
1100 N / 5cm |
800 N / 5cm |
800 N / 5cm |
1000 N / 5cm |
1800 N / 5cm |
>800 N / 5cm |
| Breaking Strength-CMD(weft) |
1300 N / 5cm |
1500 N / 5cm |
1500 N / 5cm |
1200 N / 5cm |
1300 N / 5cm |
1300 N / 5cm |
1800 N / 5cm |
>900 N / 5cm |
| Breaking Elongation(N/5cm)-MD(warp) |
20% |
35% |
20% |
5% |
25% |
20% |
10% |
<20% |
| Breaking Elongation(N/5cm)-CMD(weft) |
40% |
50% |
39% |
30% |
25% |
40% |
10% |
<25% |
| Dry Shrinkage MD(130ºCwarp) |
<1% |
<1% |
<1% |
<1% |
<1% |
<1% |
<1.5% |
<1.5% |
| Dry Shrinkage CMD(130ºCweft) |
<1% |
<1% |
<1% |
<1% |
<1% |
<1% |
<1.5% |
<1.5% |
| Operating Temperatures |
<130 deg C |
<90 deg C |
<190 deg C |
<260 deg C |
<140 deg C |
<204 deg C |
<220 deg C |
<260 deg C |
| Recommended Maximum Continuous |
130 deg C |
90 deg C |
190 deg C |
260 deg C |
140 deg C |
204 deg C |
220 deg C |
260deg C |
| Recommended Maximum Surge |
150 deg C |
110 deg C |
230 deg C |
280 deg C |
160 deg C |
240 deg C |
240 deg C |
280deg C |
PE filter bag is applicable to cement,iron and steel industries,wood processing,flour plant;
PP filter bag is applicable to food,flour,sugar,fertilizer,electroplating and pesticide industries;
PPS is applicable to the working conditions with low oxidation gas from coal-fired boiler,waste incineration,metal smelting and chemical industries;
P84 is applicable to working condition with corrosive gas,such as chemical,metal smelting,waste incineration industries,cement kiln and coal-fired boiler;
Nomex is applicable to asphalt,non-ferrous metal production,ceramic,glass industries,kiln in cement factories and blast furnace in steel factory.
Fiberglass and PTFE filter bags that can be applicable to the working condition with high corrosive gas and high temperature,such as chemical industry,coal-fired boiler,waste incineration industry and non-ferrous metal production.
Shanghai Sffiltech Co.,Ltd(Shanghai Filterbag Factory Co.,Ltd)
Our company has grown up to be one of the leading companies on the dust and liquid filtration & separation products in China, who specialized in meeting the different customers, requirements and applications.We have more than 100 kinds of filtration products such as: polyester, aramid, PPS, acrylic, fiberglass, P84, PTFE, HST, and Basalt in different finishing etc. We have 6 needle punched felt production line and on© PTFE membrane lamination line. Annual production capacity of high temperature resistance fabric has reached 6,000,000 square meters.
We also supply related spare parts of baghouse: filter cage, venture. Customized products can be made according to customer's drawing.