Fiberglass Filter Bag Dust Collection Filter Bag Woven glass High Temperature
| Shanghai Filterbag Factory Co Ltd |
Sffiltech Fiberglass |
| |
|
|
|
| 340gsm woven fiberglass with PTFE membrane |
Material |
| Warp |
US glass system |
DE75 1/0 |
| Tex system |
EC6 66 |
| Weft |
US glass system |
DE75 1/2(T) |
| Tex system |
EC6 66x2(T) |
| Thread Count |
No./inch |
54x30 |
| No./cm |
21x12 |
| Weight |
oz/sq.yd |
10 |
| g/sqm |
340±(10%) |
| Thickness |
mm |
0.4±0.1 |
| Finish |
PTFE membrane |
| Tensile Strength |
Warp |
lbs/inch |
≥308 |
| N/25mm |
≥1400 |
| Weft |
lbs/inch |
≥176 |
| N/25mm |
≥800 |
| Air Permeability |
l/dm2/min@200 Pa |
>25 |
| Operating Temperature |
Continuous |
oC |
≤260 |
| Instant |
oC |
300 |
| 450gsm woven fiberglass+PTFE membrane |
Material |
| Warp |
US glass system |
DE75 1/2 |
| Tex system |
EC6 66x2 |
| Weft |
US glass system |
DE75 13(T) |
| Tex system |
EC6 66x3(T) |
| Thread Count |
No./inch |
44x24 |
| No./cm |
17.5x9.5 |
| Weight |
oz/sq.yd |
13 |
| g/sqm |
450(±5%) |
| Thickness |
mm |
0.5±0.1 |
| Finish |
ptfe membrane |
| Tensile Strength |
Warp |
lbs/inch |
≥440 |
| N/25mm |
≥2000 |
| Weft |
lbs/inch |
≥264 |
| N/25mm |
≥1200 |
| Air Permeability |
m3/M2/min at 127Mpa |
9-17 |
| Operating Temperature |
Continuous |
oC |
≤260 |
| Instant |
oC |
300 |
| 500gsm woven fiberglass+PTFE membrane |
Material |
| Warp |
US glass system |
DE75 1/2 |
| Tex system |
EC6 66x2 |
| Weft |
US glass system |
DE75 13(T) |
| Tex system |
EC6 66x3(T) |
| Thread Count |
No./inch |
44x24 |
| No./cm |
17.5x9.5 |
| Weight |
oz/sq.yd |
14 |
| g/sqm |
500(±5%) |
| Thickness |
mm |
0.5±0.1 |
| Finish |
PTFE membrane |
| Tensile Strength |
Warp |
lbs/inch |
≥440 |
| N/25mm |
≥2000 |
| Weft |
lbs/inch |
≥264 |
| N/25mm |
≥1200 |
| Air Permeability |
m3/M2/min at 127Mpa |
3-6 |
| Operating Temperature |
Continuous |
oC |
≤260 |
| Instant |
oC |
300 |
| 750gsm woven fiberglass with PTFE membrane |
Material |
| Warp |
US glass system |
DE75 1/2 |
| Tex system |
EC6 66x2 |
| Weft |
US glass system |
DE75 2/2(T) |
| Tex system |
EC6 66x2x2(T) |
| Thread Count |
No./inch |
48x40 |
| No./cm |
19x16 |
| Weight |
oz/sq.yd |
22 |
| g/sqm |
750(±5%) |
| Thickness |
mm |
0.8±0.1 |
| Finish |
ptfe membrane |
| Tensile Strength |
Warp |
lbs/inch |
≥528 |
| N/25mm |
≥2400 |
| Weft |
lbs/inch |
≥440 |
| N/25mm |
≥2000 |
| Air Permeability |
m3/M2/min at 127Mpa |
2-5 |
| Operating Temperature |
Continuous |
oC |
≤260 |
| Instant |
oC |
300 |
| 800gsm fiberglass with PTFE membrane |
Material |
| Warp |
US glass system |
DE75 1/2 |
| Tex system |
EC6 66x2 |
| Weft |
US glass system |
DE75 2/2(T) |
| Tex system |
EC6 66x2x2(T) |
| Thread Count |
No./inch |
48x40 |
| No./cm |
19x16 |
| Weight |
oz/sq.yd |
22 |
| g/sqm |
800(±5%) |
| Thickness |
mm |
0.8±0.1 |
| Finish |
ptfe membrane |
| Tensile Strength |
Warp |
lbs/inch |
≥528 |
| N/25mm |
≥2400 |
| Weft |
lbs/inch |
≥440 |
| N/25mm |
≥2000 |
| Air Permeability |
m3/M2/min at 127Mpa |
2-5 |
| Operating Temperature |
Continuous |
oC |
≤260 |
| Instant |
oC |
300 |
| Construction |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
Needle felt |
| Fibre Composition |
polyester |
polypropylene |
PPS |
polyimide |
Acrylic |
Aramid/Nomex |
FMS |
PTFE Fiber |
| Scrim Composition |
polyester |
polypropylene |
PPS |
polyimide |
Acrylic |
Aramid/Nomex |
fiberglass |
pffe |
| Felt Area Weight |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
500g/m2(±5%) |
850g/m2(±5%) |
750g/m2(±5%) |
| Thickness |
1.8-2.0mm |
2-2.1mm |
1.7-1.9mm |
1.9-2.1mm |
1.7-2.1mm |
1.9-2.1mm |
2.8mm |
1.3-1.7mm |
| Mean Air Permeability |
10-15 m3/m2/min at 12.7mmH2O |
10-12 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
8-12 m3/m2/min at 12.7mmH2O |
10-15 m3/m2/min at 12.7mmH2O |
8-15 m3/m2/min at 12.7mmH2O |
2-5 m3/m2/min at 12.7mmH2O |
| Breaking Strength-MD(warp) |
900 N / 5cm |
1000 N / 5cm |
1100 N / 5cm |
800 N / 5cm |
800 N / 5cm |
1000 N / 5cm |
1800 N / 5cm |
>800 N / 5cm |
| Breaking Strength-CMD(weft) |
1300 N / 5cm |
1500 N / 5cm |
1500 N / 5cm |
1200 N / 5cm |
1300 N / 5cm |
1300 N / 5cm |
1800 N / 5cm |
>900 N / 5cm |
| Breaking Elongation(N/5cm)-MD(warp) |
20% |
35% |
20% |
5% |
25% |
20% |
10% |
<20% |
| Breaking Elongation(N/5cm)-CMD(weft) |
40% |
50% |
39% |
30% |
25% |
40% |
10% |
<25% |
| Dry Shrinkage MD(130ºCwarp) |
<1% |
<1% |
<1% |
<1% |
<1% |
<1% |
<1.5% |
<1.5% |
| Dry Shrinkage CMD(130ºCweft) |
<1% |
<1% |
<1% |
<1% |
<1% |
<1% |
<1.5% |
<1.5% |
| Operating Temperatures |
<130 deg C |
<90 deg C |
<190 deg C |
<260 deg C |
<140 deg C |
<204 deg C |
<220 deg C |
<260 deg C |
| Recommended Maximum Continuous |
130 deg C |
90 deg C |
190 deg C |
260 deg C |
140 deg C |
204 deg C |
220 deg C |
260deg C |
| Recommended Maximum Surge |
150 deg C |
110 deg C |
230 deg C |
280 deg C |
160 deg C |
240 deg C |
240 deg C |
280deg C |
Shanghai Sffiltech Co.,Ltd(Shanghai Filterbag Factory Co.,Ltd)
Our company has grown up to be one of the leading companies on the dust and liquid filtration & separation products in China, who specialized in meeting the different customers, requirements and applications.We have more than 100 kinds of filtration products such as: polyester, aramid, PPS, acrylic, fiberglass, P84, PTFE, HST, and Basalt in different finishing etc. We have 6 needle punched felt production line and on© PTFE membrane lamination line. Annual production capacity of high temperature resistance fabric has reached 6,000,000 square meters.
We also supply related spare parts of baghouse: filter cage, venture. Customized products can be made according to customer's drawing.
){kind=link}